Next Nylon 6 Prime Series NGF05-01BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rutq2F_Next-Nylon-6-Prime-Series-NGF05-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Glass Fiber Reinforce FR Black Compound Product Applications Industrial controls and Electrical insulating system Benefits This grade provides UL-94 V0 While offering good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.23 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.65 | -- | % | ASTM D955 |
| Transverse flow | 1.1 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.8 | -- | % | ASTM D570 |
| Saturation 1 | 7.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 95 | -- | ASTM D785 | |
| Class r | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 2600 | MPa | ASTM D638 |
| Tensile Strength | 80.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | 15 | % | ASTM D638 |
| Flexural Modulus | 3100 | 2500 | MPa | ASTM D790 |
| Flexural Strength | 130 | 85.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 180 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 145 | -- | °C | ASTM D648 |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | 26 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | UL 94 | |
| 1.60 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.60 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 750 | -- | °C | IEC 60695-2-13 |
| 1.60 mm | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 230 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BONDYRAM® 1101 | Polyram Ram-On Industries | PP Homopolymer | BONDYRAM® |
| Keysor PVC KC1101 | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| Petrothene® NA443023 (Blown) | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 7833-75 Grey 9471 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4200-85UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |