LNP™ STAT-KON™ DEI13F compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RulUV4_LNP-STAT-KON-DEI13F-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DEI13F is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 2% Silicone. Added features of this material include: Electrically Conductive, Superior Molding, Wear Resistant. Also known as: LNP* STAT-KON* Compound DCL-4413 SM Product reorder name: DEI13F |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.10 to 0.30 | % | |
| Flow 1 | 1.0E-3 to 3.0E-3 | % | |
| Across Flow 2 | 2.0E-3 to 4.0E-3 | % | |
| Across Flow | 0.20 to 0.40 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 10400 | MPa | ASTM D638 |
| -- | 10100 | MPa | ISO 527-2/1 |
| Tensile Strength (Break) | 116 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 1.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 7500 | MPa | ASTM D790 |
| -- | 9790 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 167 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.24 | ||
| vs. Itself - Static | 0.24 | ||
| Wear Factor - Washer | 343 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 4 | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D4812 |
| 23°C 5 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 25.0 | J | ASTM D3763 |
| -- | 103 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 6 | 142 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 9.0E-6 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 0.75 to 2.3 mm |
| 3 . | 50 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-CO-10GF | Pro Polymers | PP Copolymer | Pro-Comp™ |
| APEX® 4020 | Teknor Apex Company | PVC, Flexible | APEX® |
| CompaDur® 121 GF 30 natural (005) | DimeLika Plast GmbH | PBT | CompaDur® |
| Ensinger PVC | Ensinger Inc. | PVC, Unspecified | Ensinger |
| Karina WHITE PVC COMP -E 856-10/101-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |