RTP 1000 TFE 20 SI 5
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RuOu2O_RTP-1000-TFE-20-SI-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 143 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.4 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Tensile Elongation, ASTM D-638: 10+% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 232 - 271 | °C | |
| Front Temperature | 232 - 271 | °C | |
| Mold Temperature | 37.8 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-HOCC-30GF | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| Sanren M1300R (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| PENTAMID A GV35 HYD schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| P-FLEX R 2620 | Putsch Kunststoffe GmbH | ABS | P-FLEX |
| Mitsui EPT™ 3092PM | Mitsui Chemicals, Inc. | EPDM | Mitsui EPT™ |