Lotader® 8200
| Category: | EEA , Ethylene Ethyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotader® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RtxvsQ_Lotader-8200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTADER® 8200 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications Due to its properties, reactivity, fluidity and compatibility with tackifying resins and waxes, LOTADER® 8200 is suitable as additive for hot melt adhesive formulations and as coupling agent in mineral filled compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 200 | g/10 min | ASTM D1238, ISO 1133 |
| Ethyl Acrylate Content | 6.5 | wt% | |
| Maleic Anhydride Content | 2.8 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 26 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 6.00 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 400 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 40.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 57.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 100 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCUDIA® HDPE 45060-UV | REPSOL | HDPE | ALCUDIA® HDPE |
| Clariant Nylon 6/6 PA-113CF30 TF15 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Hanwha Total PE P110A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| LNP™ THERMOCOMP™ IF004 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| Ultramid® A3WG10 CR BK00564 | BASF Corporation | Nylon 66 | Ultramid® |