Order Products : sales@su-jiao.com
Orevac® 18410/18342N
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Arkema |
| Trademark: | Orevac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RtlHpA_Orevac-18410-18342N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OREVAC® 18410/18342N is a maleic anhydride modified high-density polyethylene used in pipe-coating technology for multi-layer structures. It is available in pellet form for use in conventional extrusion equipment designed to process polyolefin. Applications OREVAC® 18410/18342N has been designed to develop a reliable bonding strength onto FBE (Fusion Bonded Epoxy) steel pipe protective layer. It is mainly used as tie layer in three-layer high-density polyethylene coatings (epoxy primer / adhesive / polyethylene), where mechanical and adhesive performances at high temperatures are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 59 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 310 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break, Compression Molded) | > 20.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | > 600 | % | ASTM D638, ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 1 | 110 | °C | ISO 306/A, ASTM D1525 2 |
| Melting Temperature | 125 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 to 200 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 200 to 210 | °C | |
| Cylinder Zone 4 Temp. | 210 to 220 | °C | |
| Cylinder Zone 5 Temp. | 220 to 230 | °C | |
| Die Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | On compression molded samples |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) M/SHI | A. Schulman Europe | ABS | POLYMAN® |
| Premi-Glas® 2206-25 CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| AKROMID® A3 GF 25 1 L black (4672) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| APEX® 02-A0111A-90NT | Teknor Apex Company | PVC, Flexible | APEX® |
| DENKA Transparent Polymer CL-430 | Denka Company Limited | ABS | DENKA Transparent Polymer |