Bayfill® 369 (38:100)
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayfill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RsOdip_Bayfill-369-38-100-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bayfill 369 is a semi-rigid polyurethane foam system designed for automotive interior applications. The Bayfill 369 system is an excellent choice for the production of soft-touch panels, such as instrument panels, door trim, and center consoles. The foam is typically molded in a back-filling process between a soft, exterior skin and a rigid, thermoplastic substrate. The Bayfill 369 system is supplied as two components. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a polyol mixture. As with any product, use of the Bayfill 369 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molded Density | 147 | kg/m³ | ASTM D3574A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compression Force Deflection | ASTM D3574C | ||
| -- 1 | 0.0689 | MPa | ASTM D3574C |
| -- 2 | 0.0207 | MPa | ASTM D3574C |
| Compression Set | ASTM D3574D | ||
| Cd 3 | 66 | % | ASTM D3574D |
| Cd 4 | 33 | % | ASTM D3574D |
| Ct 5 | 16 | % | ASTM D3574D |
| Ct 6 | 33 | % | ASTM D3574D |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 7 | 0.0965 | MPa | ASTM D3574K |
| -- | 0.241 | MPa | ASTM D3574E |
| Tensile Elongation | |||
| Fracture 8 | 46 | % | ASTM D3574K |
| Fracture | 61 | % | ASTM D3574E |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 0.123 | kN/m | ASTM D3574F |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 42 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 60 cps Flash Point PMCC: 149°C NCO: 32.2 wt% Part B Type: Polyol Appearance: Colorless to light tan viscous liquid Specific Gravity @ 25°C: 1.03 Viscosity @25°C: 1100 cps Flash Point PMCC: 117°C Water: 2 wt% Hydroxyl Number: 70 KOH/g Mold Temperature: 38 to 43°CDemold Time: >90 secHand Mix Reactivity at 25°C Cream Time: 9 to 17 sec Top of Cup Time: 36 to 50 sec Gel Time: 39 to 53 to sec Rise Time: 67 to 83 sec Free-Rise Density: 4.90 to 5.70 lb/ft³ Machine Reactivity at 27 to 32°C Cream Time: 6 to 10 sec Top of Cup Time: 20 to 22 sec Gel Time: 27 to 31 sec Rise Time: 44 to 48 sec Free-Rise Density: 4.00 to 5.00 lb/ft³ Molded Density: 7 to 10.5 lb/ft³ |
| Note Message | |
|---|---|
| 1 . | 0.5 |
| 2 . | After J2 Autoclave |
| 3 . | After J2 Autoclave, Cd=compression set as a percentage of the original deflection |
| 4 . | 50, Cd=compression set as a percentage of the original deflection |
| 5 . | 50%, Ct=compression set as a percentage of the original thickness |
| 6 . | After J2 Autoclave, Ct=compression set as a percentage of the original thickness |
| 7 . | Dry Heat Aged at 140°C |
| 8 . | Dry Heat Aged at 140°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B33 | NUREL, S.A. | Nylon 6 | Promyde® |
| Ultralloy™ 3310 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Akulon® Ultraflow K-FG5 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Braskem PP H 606 | Braskem | PP Homopolymer | Braskem PP |
| INELEC ABSCF30 | Infinity LTL Engineered Compounds | ABS | INELEC |