LNP™ THERMOCOMP™ YX12401 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RriENW_LNPTHERMOCOMPYX12401compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* YX12401 is a compound based on Polyester Elastomer containing proprietary fillers. Also known as: LNP* THERMOCOMP* Compound YX12401 Product reorder name: YX12401 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 2.2 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.2 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.32 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 382 | MPa | ASTM D638 |
| -- | 412 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 22.0 | MPa | ASTM D638 |
| Yield | 22.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 33.0 | MPa | ASTM D638 |
| Fracture | 31.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 28 | % | ASTM D638 |
| Yield | 28 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 5 | 321 | MPa | ASTM D790 |
| -- 6 | 318 | MPa | ISO 178 |
| Flexural Stress | 14.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 33.0 | J | ASTM D3763 |
| -- | 41.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 112 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 7 | 87.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 47.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 8 | 49.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.0E-4 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 1.7E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 - 193 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 227 - 238 | °C | |
| Processing (Melt) Temp | 216 - 238 | °C | |
| Mold Temperature | 27 - 54 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E890 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| HiFill® PA6/6 GF/M36 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| PLUSTEK PB340S4 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| POLYfill PP CV8030 LR UV | Polykemi AB | PP, Unspecified | POLYfill |
| LNP™ STAT-KON™ MD000ISC compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |