LNP™ KONDUIT™ OX10324 compound
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RqGiUm_LNPKONDUITOX10324compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP KONDUIT* OX10324 is a compound based on PPS resin. Added feature of this grade is: Thermally Conductive. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.75 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.20 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | Internal method, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13500 | MPa | ASTM D638 |
| -- | 14000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 49.0 | MPa | ASTM D638 |
| Fracture | 53.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 0.60 | % | ASTM D638 |
| Fracture | 0.60 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 15600 | MPa | ASTM D790 |
| -- 5 | 13500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 73.0 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 24 | J/m | ASTM D256 |
| 23°C 7 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D4812 |
| 23°C 8 | 7.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 275 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 258 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 231 | °C | ISO 75-2/Af |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 1.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 1.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : -30 to 80°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | |||
| -- 10 | 3.5 | W/m/K | ASTM E1461 |
| -- 11 | 15 | W/m/K | ASTM E1461 |
| -- 12 | 1.3 | W/m/K | ISO 22007-2 |
| -- 13 | 18 | W/m/K | ISO 22007-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 2.5E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.20 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Shot Size | 50 - 75 | % | |
| Rear Temperature | 316 - 343 | °C | |
| Middle Temperature | 316 - 343 | °C | |
| Front Temperature | 316 - 343 | °C | |
| Processing (Melt) Temp | 321 - 349 | °C | |
| Mold Temperature | 110 - 150 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | through-plane, 10*10*3mm sample |
| 11 . | in-plane, ø25*0.4mm disc |
| 12 . | through-plane, 60*60*3mm plaque |
| 13 . | in-plane, 60*60*3mm plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Industrial Series NG15-02JBK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Industrial Series |
| ELIX™ ABS P3M-AT | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| G-Lene I24A530 | Gas Authority of India Limited | LLDPE | G-Lene |
| Karina GREEN PVC COMPOUND 861-40/28-IS RG (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 6034-85 Blue 8426 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |