Order Products : sales@su-jiao.com
Infino GW-1010
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RqGIBY_Infino-GW-1010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino GW-1010 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 3.20 mm | 0.53 to 0.65 | % | ISO 2577 |
| Flow : 3.20 mm | 0.51 to 0.62 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 59.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/50 |
| Break | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2000 | MPa | ASTM D790 |
| -- 3 | 2040 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 78.0 | MPa | ASTM D790 |
| -- 5 | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 62 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 790 | J/m | ASTM D256 |
| 23°C 7 | 80 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 137 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ SY 89-23-7 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Qenos PE HD0490 | Qenos Pty Ltd | HDPE | Qenos PE |
| Milastomer™ S-250B | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| SLOVAMID® 66 GF 20 GB 10 HI | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Evoprene™ G 978 | AlphaGary | SEBS | Evoprene™ G |