NOVAREX® 7022R
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | NOVAREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RppFnr_NOVAREX-7022R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NOVAREX®7022R is a polycarbonate (PC) material,. This product is available in the Asia-Pacific region,. NOVAREX®The main characteristics of 7022R are: low viscosity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.60 | % | ISO 294-4 |
| Flow direction | 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.9 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 67 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 6.0E-4 | IEC 60250 | |
| 1 MHz | 9.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V500/30GC | Lucent Polymers, Inc. | PP Homopolymer | Primefin |
| SCHULAKETON NV | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |
| ACCUTECH™ CP0437C10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| DENISTAT P 20C 02 C | Vamp Tech | PP Copolymer | DENISTAT |
| Durethan® BC 30 S 000000 | LANXESS GmbH | Nylon 6 | Durethan® |