SCHULAMID® 66 MV HI K1416
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rpo3o6_SCHULAMID-66-MV-HI-K1416.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Higher impact Polyamide 66 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Saturation, 23°C) | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2100 | 750 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 55.0 | 40.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.5 | 25 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 40 | > 100 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1950 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 75.0 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 7.0 | -- | % | ISO 176 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 18 | -- | kJ/m² | |
| 23°C | 65 | 95 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 140 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | > 250 | -- | °C | ISO 306/A50 |
| -- | 210 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 23 | -- | mm/min | ISO 3795 |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 650 | °C | |
| 3.00 mm | -- | 650 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PS 6L5 | Witcom Engineering Plastics B.V. | PS (GPPS) | Witcom PS |
| NEFTEKHIM PP 1462R (HOXP817) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Elastollan® 1254 D U | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| Hylon® N1043HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Sylvin 4222-90LG Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |