Description High Impact Application Gears |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.7 to 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 41.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 150 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1480 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 54.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 135 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Minimum Moisture Content | 0.10 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 170 to 190 | °C | |
| Front Temperature | 180 to 200 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.495 to 3.04 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® BP2200 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| NYLEM® 6 GFR 20 IM | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| AEI SX-0610:CM601 | AEI Compounds Limited | XLPE | AEI |
| EMOPLEN® CP GFR 30 UV | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| SCHULABLEND® (ABS/PC) M/MB 4302 PG | A. Schulman Europe | PC+ABS | SCHULABLEND® |