Veradel® A-101
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Veradel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rp232Z_VeradelA101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RADEL A polyethersulfone resin has high thermal deformation temperature, excellent toughness and dimensional stability, and is resistant to water vapor, boiling water and inorganic acids. Other excellent properties include thermal stability, creep resistance and inherent flame retardancy. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ASTM D638 |
| Tensile Strength | 83.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 6.5 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 111 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 85 | J/m | ASTM D256 |
| Tensile Impact Strength | 336 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| CLTE - Flow | 4.9E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (0.8 mm) | 180 | °C | UL 746 |
| RTI Imp (0.8 mm) | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.7E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.51 | ASTM D150 | |
| 1 kHz | 3.50 | ASTM D150 | |
| 1 MHz | 3.54 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.7E-3 | ASTM D150 | |
| 1 kHz | 2.2E-3 | ASTM D150 | |
| 1 MHz | 5.6E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-0 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 2.5 | hr | |
| Cylinder Zone 1 Temp. | 327 - 371 | °C | |
| Melt Temperature | 343 - 390 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-4100-GF10 | QTR, Inc. | PPE+PS | QR Resin |
| VITAMIDE® BI72NT6506 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| NEXT REGRIND PBT DR51-300RG | NEXT Specialty Resins, Inc. | PBT | NEXT REGRIND |
| GLS PP YN06 HF2 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| Larton GCE/600 | LATI S.p.A. | PPS | Larton |