Ultramid® A3HG6 WIT
| Category: | Nylon 6T/66 , Polyamide 6T/66 Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RoriIL_Ultramid-A3HG6-WIT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre reinforced injection moulding grade with good resistance to hydrolysis, suited for processing by water injection technology (WIT). Applications in the automotive cooling circuit, e.g. cooling water pipes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 8.00 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.86 | -- | % | ISO 294-4 |
| Flow direction | 0.37 | -- | % | ISO 294-4 |
| Viscosity Number (96% H2SO4) | 146 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.36 | -- | % |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | (PA66+PA6T/6)-(GF+GB)30 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8700 | 5300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 165 | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 4.9 | % | ISO 527-2 |
| Flexural Modulus | 7900 | 4900 | MPa | ISO 178 |
| Flexural Stress | 250 | 150 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | 85 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 230 | -- | °C | ISO 75-2/A |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 290 | °C | |
| Middle Temperature | 290 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 0692N-NE | TSRC Corporation | SEBS | T-Blend® |
| TRIBOCOMP® PC GF30 TS0 | EPIC Polymers | PC | TRIBOCOMP® |
| Iupilon® MB1700 | Mitsubishi Engineering-Plastics Corp | PC+ABS | Iupilon® |
| OTECH ALLOY OE8522 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| LNP™ STAT-KON™ DSL229 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |