VAMPLEN 3026 V0 CB DF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rof9hf_VAMPLEN-3026-V0-CB-DF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0 at 0,8 mm, 30% glass fiber reinforced, chemically bonded, RoHS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 0.70 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648A |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 1 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 to 2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3299 X 120869 A NAT/BLK | RTP Company | ETFE | RTP |
| Alcryn® 4070 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| KRATON® D1165 P | Kraton Polymers LLC | SIS | KRATON® |
| LNP™ THERMOCOMP™ RX04515H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| POLYFORT® FIPP 30 T K1005 | A. Schulman Europe | PP Copolymer | POLYFORT® |