Generic ABS+PC - Carbon Fiber, Nickel-Coated
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RoWAzO_Generic-ABS-PC---Carbon-Fiber-Nickel-Coated.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+PC - Carbon Fiber, Nickel-Coated This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 - 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.10 - 0.25 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5800 - 14600 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 67.6 - 99.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 0.50 - 1.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5200 - 13800 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 95.0 - 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 52 - 66 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 180 - 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 99.0 - 121 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 0.20 - 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 0.030 - 25 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.1 - 98.9 | °C | |
| Drying Time | 3.5 - 4.5 | hr | |
| Suggested Max Moisture | 0.020 - 0.040 | % | |
| Suggested Max Regrind | 18 | % | |
| Rear Temperature | 259 - 268 | °C | |
| Middle Temperature | 260 - 268 | °C | |
| Front Temperature | 260 - 268 | °C | |
| Nozzle Temperature | 263 - 268 | °C | |
| Processing (Melt) Temp | 259 - 268 | °C | |
| Mold Temperature | 45.0 - 86.1 | °C | |
| Back Pressure | 0.345 - 2.03 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+PC - Carbon Fiber, Nickel-CoatedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 94-A0098A-60 | Teknor Apex Company | PVC, Flexible | APEX® |
| Kingfa HC-110 | Kingfa | ABS | Kingfa |
| Latimass 52/11-04 D008 | LATI S.p.A. | PP Homopolymer | Latimass |
| Karina LILAC PVC COMP -E KAPU 6534/190-NT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Ultrathene® UE672102X02 | LyondellBasell Industries | EVA | Ultrathene® |