AKROMID® A3 ICF 20 S1 black (5057)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ro6gX8_AKROMID-A3-ICF-20-S1-black-5057-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 ICF 20 S1 black (5057) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties Applications are mechanically high stressed parts in all industries |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.18 | -- | g/cm³ | ISO 1183 |
| Humidity Absorption - 62% RH (70°C) | 1.9 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 3.0 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 20 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11100 | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 10000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 210 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 50 | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1486 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Telcar® OBC 4876N | Teknor Apex Company | TPE | Telcar® |
| Abstron HCR-15 M | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Elastron® V V100.A78.N | Elastron USA, Inc. | TPV | Elastron® V |
| Karina IVORY PVC COMPOUND 105900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |