RELENE® 45GP004
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RnZdq8_RELENE-45GP004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Relene 45GP004 ( PE:80 ) is a natural coloured grade for pipe extrusion. It possesses bimodal molecular weight distribution, which improves processability. This grade meets the MFI, Density & Hydrostatic strength requirements of material grade PE:80 as per IS 4984. When incorporated with adequate quantity of carbon black as specified in clause 5.2.3 of IS: 4984, Pipes will meet PE:80 requirements . Pipe made from Relene 45GP004 grade passes the Internal Pressure Creep Rupture Test when tested with 4.6 MPa induced stress at 80°C for 165 hrs and with 4.9 MPa induced stress at 80°C for 48 hrs as per clause 8.1 of IS 4984, thereby meeting the requirement of PE:80 grade. This grade conforms to ISO 4427 specification shown below and has been certified for MRS > 8 MPa as per ISO 9080. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.45 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Compression Molded) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | > 600 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 800 | MPa | ASTM D790 |
| Hydrostatic Pressure Test | ISO 1167 | ||
| 20°C 1 | > 4.2 | day | |
| 80°C 2 | > 41.7 | day | |
| 80°C 3 | > 6.9 | day |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 30 | min | ASTM D3985 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS | > 8.00 | MPa | ISO 9080 |
| SCG | > 20.8 | day | ISO 13479 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | No Break | ASTM D256 |
| Note Message | |
|---|---|
| 1 . | 9 MPa |
| 2 . | 4.0 MPa |
| 3 . | 4.6 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP740T | PolyMirae | PP Random Copolymer | Moplen |
| UNITIKA Nylon 66 BV2120G30 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| ASTABLEND™ MNM19 | Marplex Australia Pty. Ltd. | ABS+Nylon | ASTABLEND™ |
| LNP™ STAT-KON™ DEL33EC compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Sylvin 6168-80 Grey 9557 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |