Devcon DFense Blok™
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rll6mh_Devcon-DFense-Blok-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFense Blok™ is a revolutionary wear and abrasion alumina ceramic bead-filled epoxy compound. DFense Blok™ is formulated to significantly outlast traditional wear and abrasion products while also providing superior peformance in the most severe conditions. Intended Use:
Product Features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.21 | g/cm³ | |
| Specific Volume | 0.455 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 149 | °C | |
| Wet | 60 | °C | |
| Tensile Shear Adhesion | 18.0 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.050 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | 54.3 | MPa | ASTM D790 |
| Compressive Strength | 49.3 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 5.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | 49.0 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100 Mixing ratio by capacity: 2.0 | ||
| Component B | Mixing ratio by weight: 45 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 25 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP203L | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| THERMOLAST® K TC8SCE (Series: SCR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Abstron IM11GMS | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Hanwha Total PP CB76S | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hanwha Total PE EP32 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |