Durethan® BKV 215 H3.0 000000
| Category: | Nylon 6 , Polyamide Copolymer |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RlhpSB_DurethanBKV215H30000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.18 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 3.00mm 1 | 0.83 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.15 | -- | % | ISO 2577 |
| Flow direction : 280°C, 3.00mm 3 | 0.30 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.050 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4500 | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.5 | 15 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 4200 | 2300 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 125 | 55.0 | MPa | ISO 178/A |
| 23°C 6 | 135 | 75.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 5.5 | 8.5 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/66-HI, GHR, 14-040, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 70 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C | 20 | 35 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | 60 | kJ/m² | ISO 180/1U |
| 23°C | 60 | 90 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 175 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 214 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.7E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Oxygen Index 9 | 22 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 400 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 400 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FP62E13 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| RheTech Polypropylene HP514-393 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Terluran® HI-10 | INEOS Styrolution Group GmbH | ABS | Terluran® |
| WPP PP PPTFFR-2 | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP PP |
| LEXAN™ 103R resin | SABIC Innovative Plastics | PC | LEXAN™ |