SABIC® PP 83MF10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rkunxy_SABIC-PP-83MF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines a very high impact strength, even at low temperatures, with a high stiffness and moderate flow properties. It is suitable for injection moulding of technical components and containers exposed to heavy loads and needing a high toughness. It is also suitable for extrusion applications like thin sheet, corrugated board and profiles. It is also available in an UV-stabilized version. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 | |
| Shore Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1250 | MPa | ASTM D638 |
| -- | 1200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 23.0 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | |
| 0°C | 40 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C | 130 | J/m | ASTM D256A |
| 0°C | No Break | ASTM D256A, ISO 180/1A | |
| 23°C | No Break | ASTM D256A, ISO 180/1A | |
| -20°C | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 68.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP HDPE 055952 | Amco Polymers | HDPE | PRIMATOP |
| Vital-Line SHE5020G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Beamset 243NS | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
| ESTABLEND 4500 T V0 | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| Sylvin 3299-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |