Sarlink® TPE ML-1140B BLK X (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RkNXc8_Sarlink-TPE-ML-1140B-BLK-X-PRELIMINARY-DATA-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink ML-1140B BLK X is a general purpose TPE designed for automotive interior applications. This is a low hardness, high density grade suitable for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 44 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 41 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 39 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 0.800 | MPa | ISO 37 |
| Flow : 100% strain | 1.20 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 4.30 | MPa | ISO 37 |
| Flow : Fracture | 3.40 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 890 | % | ISO 37 |
| Flow : Fracture | 750 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 17 | kN/m | ISO 34-1 |
| Flow | 18 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 22 | % | ISO 815 |
| 70°C, 22 hr | 37 | % | ISO 815 |
| 90°C, 70 hr | 69 | % | ISO 815 |
| 125°C, 70 hr | 94 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 23 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 35 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 2.5 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 0.0 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 26 | % | ISO 188 |
| Flow : 125°C, 168 hr | 35 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | -3.8 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | -0.83 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 10 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 18 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 15 | % | ISO 188 |
| Flow : 125°C, 168 hr | 25 | % | ISO 188 |
| Change in Shore Hardness in Air | |||
| Support a, 110°C, 1008 hr 8 | -0.60 | ISO 188 | |
| Support a, 110°C, 1008 hr 9 | -0.70 | ISO 188 | |
| Support a, 110°C, 1008 hr 10 | -2.2 | ISO 188 | |
| Support a, 125°C, 168 hr 11 | 0.10 | ISO 188 | |
| Support a, 125°C, 168 hr 12 | -1.1 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 134 | Pa·s | ASTM D3835 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Xenon Weatherometer | SAE J1885 | ||
| Delta E - 1250 kJ | 0.280 | SAE J1885 | |
| Delta E - 2500 kJ | 0.220 | SAE J1885 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 5 sec |
| 9 . | 15 sec |
| 10 . | 1 sec |
| 11 . | 15 sec |
| 12 . | 1 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME GPPS SC206E | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| SUSTAPEEK GLD 140 FG blue | Röchling Sustaplast SE & Co. KG | PEEK | SUSTAPEEK |
| TARFLON™ NEO AG1950 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Bynel® 41E755 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| ESTAPROP KUR 4000 CH/TD | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |