AFFINITY™ PF 1162G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ri0g42_AFFINITY-PF-1162G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 5.94 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 5.78 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 44.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 41.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 610 | % | ASTM D882 |
| TD : Fracture, 51 µm | 650 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | > 850 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 400 | g | ASTM D1922 |
| TD : 51 µm | 510 | g | ASTM D1922 |
| Seal Initiation Temperature 1(51 µm) | 80.0 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 76.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 95.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 81 | ASTM D2457 | |
| Haze (50.8 µm) | 5.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 177 - 232 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆类型：单跨双混合 模具间隙：70 密尔 (1.8 mm) 熔体温度：350-450°F (177-232°C) 输出：模具周长的 6.5 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 |
| Note Message | |
|---|---|
| 1 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed (150 mm/s). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 360.7 | RTP Company | PC | RTP |
| Sinvicomp SFW6500S | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Algoflon® F 5 | Solvay Specialty Polymers | PTFE | Algoflon® |
| Formolene® 5143H | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Geon™ Vinyl Flexible B8000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |