Borclear™ RF366MO
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borclear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RhVTrd_Borclear-RF366MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borclear RF366MO is a specially modified highly-transparent polypropylene random copolymer with medium melt flow rate. This grade is designed for high-speed injection moulding and contains nucleating and antistatic additives. The improved processability, even at low melt temperature, allows energy savings and faster cycle time. Products originating from this grade have excellent transparency, good organoleptic properties, good balance of stiffness and impact strength at ambient temperatures. These properties, together with high gloss, make this grade excellent choice for household and packaging articles. Borclear RF366MO can be also used in injection stretch blow moulding (ISBM). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.0 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | Internal Method | ||
| 1.00 µm | 4.0 | % | |
| 2.00 µm | 10 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 30RHGF30-1.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Daelim Po1y® 5070(UV) | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Gallonprene® GP540-8004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LNP™ THERMOCOMP™ UX05504 compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| NILAMID® XS3 GF55 TF10 | Nilit Plastics | Nylon, Unspecified | NILAMID® |