BJB Polyurethane TC-892 A/B FR
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RhBw3U_BJB-Polyurethane-TC-892-A-B-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-892 A/B FR incorporates a non-mercury based catalyst system that produces a tough 80 shore D material with a 20-25 minute work time. This system can be used to hand pour large electronic housing, models of all kinds, and point of purchase items. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1810 | MPa | ASTM D638 |
| Tensile Strength | 44.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.6 | % | ASTM D638 |
| Flexural Modulus | 2270 | MPa | ASTM D790 |
| Flexural Strength | 78.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 90.6 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 83.9 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity (25°C) | 975 | cP | ASTM D2393 |
| Demold Time (25°C) | 300 - 360 | min | |
| Post Cure Time (82°C) | 16 | hr |
| Additional Information |
|---|
| Shrinkage linear, 12" x 0.5" x 0.5": 0.003 in/inMix ratio by weight: 70/100Mix ratio by volume: 79/100Work time, 100 g, 77°F: 20-25 mingel time: 30-35 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIS7068A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Thermalux® Film | Westlake Plastics Company | PSU | Thermalux® |
| EVAL™ F101 | Kuraray Co., Ltd. | EVOH | EVAL™ |
| Karina GRAY PVC COMPOUND 800-18/423-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPAMOULD 665D30 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |