MAXAMID™ PA66M40HSL-BK10
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rgmreu_MAXAMID-PA66M40HSL-BK10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™ PA66M40 is available in natural , internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8280 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 220 | °C | ASTM D648 |
| Peak Melting Temperature | 259 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Carbotex K-20T28 | Kotec Corporation | PC | Carbotex |
| CEPLA CT-453 | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| HIPOLEN P® TM 21 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| LNP™ THERMOCOMP™ KF002L compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ THERMOCOMP™ |
| POLYCOMPO PP J715M | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |