HiFill® PC 0272 S1
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rfi6a0_HiFill-PC-0272-S1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill®PC 0272 S1 is a polycarbonate (PC) product, which contains a 10% glass fiber reinforced material. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.71 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 43.4 | MPa | ASTM D638 |
| Fracture | 66.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.0 | % | ASTM D638 |
| Fracture | 8.0 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 302 - 316 | °C | |
| Middle Temperature | 316 - 332 | °C | |
| Front Temperature | 310 - 327 | °C | |
| Nozzle Temperature | 310 - 327 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A 24EPT3010UK 333 NER | Radici Plastics | Nylon 66 | Radilon® |
| Vi-Chem PVC V221-80E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| APEX® 3300-85NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina CREAM COLOR CONCENTRATE -E 20/ 15-RG-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KOPPS® S21A65BL | Kolon Plastics, Inc. | PPS | KOPPS® |