Order Products : sales@su-jiao.com
AURAPENE PPUFBKIMP
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Aurora Manufacturing Ltd |
| Trademark: | AURAPENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RfAbwm_AURAPENE-PPUFBKIMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPUFBK is a general purpose polypropylene compound with good impact performance and manufactured from recycled polymer. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 to 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.3 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 to 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1 | < 100 | mm/min | ISO 3795 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Rear Temperature | 195 to 230 | °C | |
| Middle Temperature | 195 to 230 | °C | |
| Front Temperature | 195 to 230 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUPLENE® BX3500H | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| NYCOA Polyamide 6215 HS | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| LNP™ THERMOCOMP™ RX06420 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Dynalloy™ GP 7820-60N | PolyOne Corporation | TPE | Dynalloy™ |
| 3M™ Dyneon™ Perfluoroelastomer PFE E-21464 | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |