Order Products : sales@su-jiao.com
CALP GF3010A
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | CALP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Reyl4s_CALP-GF3010A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CALP GF3010A is a Polyolefin product filled with glass fiber. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: food contact acceptable. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 0.30 | % | |
| Across Flow : 2.00 mm | 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 101 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6400 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 9.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 162 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex ST-0185 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Elastocon® SMR1450 | Elastocon TPE Technologies | TPO (POE) | Elastocon® |
| ENFLEX VL-120-40D | ENPLAST, a Ravago Group Company | TPV | ENFLEX |
| Plenco 01501 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |
| CERTENE™ HI-2053 | Muehlstein | HDPE | CERTENE™ |