LNP™ THERMOCOMP™ UF0067W compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ren1LZ_LNP-THERMOCOMP-UF0067W-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UF0067W is a compound based on Polyphthalamide resin containing 30% glass fiber. Added features of this material include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flame Retardant. Also known as: LNP* THERMOCOMP* Compound UF-1006 HW Z270 Product reorder name: UF0067W |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.20 to 0.50 | % | |
| Across Flow : 24 hr | 1.2 to 1.5 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10500 | MPa | ASTM D638 |
| -- | 11300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 143 | MPa | ASTM D638 |
| Break | 128 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.5 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 10200 | MPa | ASTM D790 |
| -- 5 | 9130 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 189 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 213 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 7 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 660 | J/m | ASTM D4812 |
| 23°C 8 | 32 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 1.86 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 299 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 281 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 277 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (0.800 mm, in Oil) | 30 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.05 | ||
| 1 MHz | 3.82 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.012 | ||
| 1 MHz | 0.013 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.50 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 280 to 320 | °C | |
| Front Temperature | 280 to 320 | °C | |
| Nozzle Temperature | 280 to 320 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LLG815W | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| YUNGSOX® PP 3005 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Baydur® 661 IBS (30 pcf, 20% Wollastocup) | Covestro - PUR | PUR-MDI | Baydur® |
| Fainplast PVC PH 65/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Ecollent™ PPC | Lucent Polymers, Inc. | PP, Unspecified | Ecollent™ |