Generic PPE+PS - Glass Fiber
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RdRNtZ_Generic-PPE-PS---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPE+PS - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 - 1.31 | g/cm³ | ASTM D792 |
| 23°C | 1.13 - 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 4.5 - 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 6.80 - 15.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.19 - 0.40 | % | ASTM D955 |
| Transverse flow : 23°C | 0.30 - 0.80 | % | ASTM D955 |
| 23°C | 0.19 - 0.61 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.054 - 0.11 | % | ASTM D570 |
| 23°C, 24 hr | 0.059 - 0.15 | % | ISO 62 |
| Saturated, 23°C | 0.060 - 0.24 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.058 - 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 104 - 108 | ASTM D785 | |
| Ball Indentation Hardness | 100 - 130 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3600 - 13800 | MPa | ASTM D638 |
| 23°C | 3660 - 11300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 58.8 - 167 | MPa | ASTM D638 |
| Yield, 23°C | 50.0 - 155 | MPa | ISO 527-2 |
| Fracture, 23°C | 66.1 - 165 | MPa | ASTM D638 |
| Fracture, 23°C | 63.1 - 155 | MPa | ISO 527-2 |
| 23°C | 75.1 - 101 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.7 - 3.1 | % | ASTM D638 |
| Yield, 23°C | 1.7 - 3.0 | % | ISO 527-2 |
| Fracture, 23°C | 1.4 - 5.2 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3190 - 11900 | MPa | ASTM D790 |
| 23°C | 3000 - 9710 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 96.1 - 169 | MPa | ASTM D790 |
| 23°C | 117 - 195 | MPa | ISO 178 |
| Yield, 23°C | 99.7 - 225 | MPa | ASTM D790 |
| Fracture, 23°C | 118 - 177 | MPa | ASTM D790 |
| Coefficient of Friction | 0.27 - 0.89 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 44.8 - 70.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.9 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 - 35 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 57 - 120 | J/m | ASTM D256 |
| 23°C | 5.8 - 12 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 8.00 - 14.1 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 260 - 650 | J/m | ASTM D256 |
| 23°C | 19 - 31 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 13.6 - 22.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 103 - 161 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 126 - 170 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 119 - 151 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 112 - 149 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 135 - 181 | °C | ASTM D1525 |
| -- | 129 - 180 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 2.0E-6 - 2.5E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.0E-5 - 6.0E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.7E-5 - 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.9E-5 - 8.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 6.7E-5 - 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.21 - 0.28 | W/m/K | ISO 8302 |
| RTI Elec | 50.0 - 110 | °C | UL 746 |
| RTI Imp | 50.0 - 106 | °C | UL 746 |
| RTI | 50.0 - 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 40 - 4.0E+17 | ohms | ASTM D257 |
| -- | 5.1E+5 - 1.3E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 50 - 1.3E+16 | ohms·cm | ASTM D257 |
| 23°C | 15 - 3.3E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 17 - 71 | kV/mm | ASTM D149 |
| 23°C | 16 - 31 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.73 - 3.17 | ASTM D150 | |
| 23°C | 2.90 - 3.40 | IEC 60250 | |
| 23°C | 2.90 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 8.0E-4 - 4.2E-3 | ASTM D150 | |
| 23°C | 4.0E-4 - 6.1E-3 | IEC 60250 | |
| Comparative Tracking Index | 172 - 252 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 750 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 750 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 26 - 36 | % | ASTM D2863 |
| -- | 23 - 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 89.3 - 121 | °C | |
| Drying Time | 2.4 - 4.5 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.021 | % | |
| Suggested Shot Size | 50 | % | |
| Hopper Temperature | 70.0 - 70.5 | °C | |
| Rear Temperature | 250 - 291 | °C | |
| Middle Temperature | 270 - 299 | °C | |
| Front Temperature | 290 - 308 | °C | |
| Nozzle Temperature | 270 - 313 | °C | |
| Processing (Melt) Temp | 279 - 313 | °C | |
| Mold Temperature | 70.0 - 108 | °C | |
| Injection Pressure | 84.5 - 86.2 | MPa | |
| Back Pressure | 0.255 - 0.517 | MPa | |
| Screw Speed | 44 - 105 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+PS - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G20P252-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sylvin 9711-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ 2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| KYDEX® XD | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |
| Delene 1140 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |