MELOPAS® MP 180
| Category: | Mel Phenolic , Melamine Phenolic |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | MELOPAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RdDP4I_MELOPAS-MP-180.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wood flour reinforced phenol-modified Melamine moulding compound Excellent surface hardness, good mechanical properties, good electrical properties, good heat resistance Primary application(s): Moulded parts in electrical engineering, mountings for household appliances, car ashtrays This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) Identification according to ISO 14528-1: MP (WD30+MD15) - (WD40+MD05) DIN 7708: MP 180 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 to 1.60 | g/cm³ | ISO 1183 |
| Apparent Density | 0.55 to 0.75 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | ISO 2577 | ||
| -- 1 | 0.50 to 0.90 | % | |
| -- 2 | 0.80 to 1.2 | % | |
| Water Absorption (23°C, 24 hr) | < 2.0 | % | ISO 62 |
| Post Shrinkage 3 | 0.80 to 1.3 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 160 | °C | |
| 20,000 h | 135 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 20.0 | MPa | |
| Compression Molding Temperature | 160 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 5000 to 8000 | MPa | |
| Injection Molded | 5000 to 8000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 45.0 to 60.0 | MPa | |
| Injection Molded | 50.0 to 70.0 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 7000 to 9000 | MPa | |
| Injection Molded | 7000 to 9000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 90.0 to 120 | MPa | |
| Injection Molded | 100 to 130 | MPa | |
| Compressive Stress | 200 to 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 1.2 to 1.8 | kJ/m² | |
| Injection Molded | 1.4 to 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 4.5 to 7.0 | kJ/m² | |
| Injection Molded | 6.0 to 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 155 to 180 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 110 to 130 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.5E-5 to 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.50 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 to 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 15 to 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 16.0 11.0 | ||
| 1 MHz | 9.00 7.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.30 to 0.50 | ||
| 1 MHz | 0.030 to 0.050 | ||
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index | > 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 900 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 70.0 to 90.0 | °C | |
| Front Temperature | 90.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 160 to 180 | °C | |
| Back Pressure | 0.800 to 1.20 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | Injection Molded |
| 3 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4003 FR | RTP Company | PPA | RTP |
| MAJORIS EG304 | AD majoris | PP, Unspecified | MAJORIS |
| Plenco 05118 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| RTP 699 X 138787 E Nat/Clear | RTP Company | ABS | RTP |
| Durethan® BKV 50 000000 | LANXESS Corporation | Nylon 6 | Durethan® |