POCAN® KU 2-7241 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rc6Xpq_POCANKU27241000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 25 % glass fibres, injection moulding, flame retardant, improved impact strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.60 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction : 260°C, 3.00mm 1 | 1.0 | % | ISO 2577 |
| Vertical flow direction : 150°C, 48 hours, 3.00mm 2 | 0.26 | % | ISO 294-4 |
| Flow direction : 260°C, 3.00mm 3 | 0.26 | % | ISO 2577 |
| Flow direction : 150°C, 48 hours, 3.00mm 4 | 0.070 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 7800 | MPa | ISO 178/A |
| Flexural Stress 6 | |||
| 3.5% strain | 190 | MPa | ISO 178/A |
| 23°C | 195 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.6 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Gottfert Melt Viscosity (260°C) | 220165 1/s | Internal method | |
| ISO Shortname | PBT, GFHMPR, 11-090, GF25; ISO 1043-PBT GF FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 110 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.80 | IEC 60250 | |
| 23°C, 1 MHz | 3.70 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Oxygen Index 9 | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x3; MT 80°C; 600 Bar |
| 2 . | 150x105x3 |
| 3 . | 150x150x3; MT 80°C; 600 Bar |
| 4 . | 150x150x3 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYVIN® PVC 6025D | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| PrimaFlex® HD 5306 | Plastic Solutions, Inc. | HDPE | PrimaFlex® |
| Tenac™-C HC760 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| NEXT SIGNATURE PA6 G33-100 | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT SIGNATURE |
| Halene H Y5401 | Haldia Petrochemicals Ltd. | HDPE | Halene H |