Lupoy® SR3108L
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RbMU9o_Lupoy-SR3108L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Flow, High Impact, White Color Only Application BLU Mold frame for Mobile Devices |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 6.40 mm) | 124 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 260 to 290 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9955H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Retpol® 7860 | PolyPacific Pty. Ltd. | Rubber | Retpol® |
| Hostacom TRC 454N D11534 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LNP™ COLORCOMP™ AX98567H compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |
| Karina CLEAR PVC COMPOUND 78/200-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |