DOW™ Butene 1221G1
| Category: | PE, Unspecified , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ Butene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rae8qG_DOW-Butene-1221G1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Force 1(25 µm) | 48.9 | N | Internal method |
| Film Puncture Resistance (25 µm) | 9.02 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm | 149 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm | 147 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 10.7 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 8.94 | MPa | ASTM D882 |
| MD : Break, 25 µm | 39.6 | MPa | ASTM D882 |
| TD : Break, 25 µm | 20.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 450 | % | ASTM D882 |
| TD : Break, 25 µm | 680 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 66 | g | ASTM D1709A |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 25 µm | 37 | g | ASTM D1922 |
| TD : 25 µm | 370 | g | ASTM D1922 |
| Film Tensile Properties-Maximum Elongation 3(25.4 µm) | 230 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.1 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 116 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 25.4 µm) | 151 | ASTM D2457 | |
| Clarity (25.4 µm) | 99.0 | ASTM D1746 | |
| Haze (25.4 µm) | 0.56 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 271 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 模具间隙：20 密尔 (0.50 mm) 熔体温度：520°F (271°C) 气隙：3 英寸 (7.6 cm) 脱离速度：600 fpm (183 mpm) |
| Note Message | |
|---|---|
| 1 . | Test on pallet, 200% prestretching |
| 2 . | Modified rectangular measuring piece |
| 3 . | Test on pallet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sultron® R40SL | Asia International Enterprise (Hong Kong) Limited | PPS | Sultron® |
| Viton® A-331C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Topolymer® 5111-801E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Zytel® SC310 NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Delene 3550 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |