| Tekumid 6 SC is a Polyamide 6 (Nylon 6) material. It is available in Europe. Primary attribute of Tekumid 6 SC: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.26 | -- | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 9.0 to 10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 to 3.4 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | 120 | 102 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield | 80.0 | 40.0 | MPa | |
| Break | 60.0 | 30.0 | MPa | |
| Tensile Elongation (Break) | > 60 | > 200 | % | ASTM D638 |
| Flexural Modulus | 2800 | 800 | MPa | ASTM D790 |
| Flexural Strength | 120 | 60.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (0°C, 3.20 mm) | 45 | 500 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 50 | 600 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 180 | -- | °C | |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | |
| Vicat Softening Temperature | ||||
| -- | 200 | -- | °C | ASTM D1525 1 |
| -- | 165 | -- | °C | ISO 306/B50 |
| Melting Temperature | 215 to 220 | -- | °C | DSC |
| CLTE - Flow (-30 to 30°C) | 7.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.25 | -- | W/m/K | ASTM C177 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | 90 | 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.60 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | -- | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | V-2 | -- | ||
| Glow Wire Ignition Temperature (2.00 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CoolPoly® D5506 | Celanese Corporation | LCP | CoolPoly® |
| CROSSVINIL EK/500 1Z | Crosspolimeri S.p.A. | PVC, Unspecified | CROSSVINIL |
| Daelim Po1y® TR-130 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Fainplast PVC KL 52/V | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Petrothene® GA818092 | LyondellBasell Industries | LLDPE | Petrothene® |