MAJORIS AN081
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RYw1KV_MAJORIS-AN081.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AN081 is a polypropylene copolymer for injection moulding, extrusion and blow moulding. APPLICATIONS AN081 is recommended for applications like:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.9 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 48.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 11 | % | |
| Break | > 300 | % | |
| Flexural Modulus 1 | 1350 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.8 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 5.5 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A |
| -- | 70.0 | °C | ISO 306/B |
| CLTE - Flow (-30 to 80°C) | 8.2E-5 | cm/cm/°C | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 40.0 to 80.0 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Holding Pressure | 30.0 to 60.0 | MPa | |
| Injection Velocity | 100 to 200 | mm/sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 220 to 260 | °C | |
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 210 to 250 | °C | |
| Cylinder Zone 3 Temp. | 210 to 250 | °C | |
| Cylinder Zone 5 Temp. | 210 to 250 | °C | |
| Melt Temperature | 220 to 260 | °C | |
| Die Temperature | 220 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® K203 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| Xuchuan XCS-4575 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Zytel® HTN FR52G30NH NC010 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Desmopan® DP 1050D | Covestro - PUR | TPU, Unspecified | Desmopan® |
| LNP™ LUBRICOMP™ KL004A compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |