| Unreinforced, Flame Retardant, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.0 | -- | % | ISO 294-4 |
| Flow | 0.90 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C, 2.00mm | 8.0 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 2.4 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness 1(H 358/30) | -- | 110 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3800 | 1800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | -- | 60.0 | MPa | ISO 527-2 |
| Fracture | 80.0 | -- | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | -- | 21 | % | ISO 527-2 |
| Fracture | 10 | -- | % | ISO 527-2 |
| Nominal Tensile Strain at Break | -- | 30 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 4.4 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 230 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 3 | -- | > 1.0E+15 | ohms | IEC 60093 |
| Dielectric Strength | 31 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 0 | -- | UL 746 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.8 mm | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.40 mm | 960 | -- | °C | IEC 60695-2-12 |
| 0.75 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.5 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.40 mm | 960 | -- | °C | IEC 60695-2-13 |
| 0.75 mm | 960 | -- | °C | IEC 60695-2-13 |
| 1.5 mm | 960 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 960 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 39 | -- | % | ISO 4589-2 |
| FMVSS Flammability | DNI | -- | FMVSS 302 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2590 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.17 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Odor | 5.00 | -- | VDA 270 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 280 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.03 | -- | g/cm³ | |
| Ejection Temperature | 210 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | Derived from Similar Grade |
| 2 . | 10°C/min |
| 3 . | based on CTI and similar values for FR grades, Assessed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUCOMP™ ABS892DL | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| BESTDUR PHG6 | Triesa Plastics | PET | BESTDUR |
| INTEGRAL™ 604 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |
| Delon 4040 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | Delon |
| Starex NT-7310 | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |