DIC.PPS FZ-928N Black
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RWytkZ_DIC-PPS-FZ-928N-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.32 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 84 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ASTM D638 |
| Tensile Strength | 135 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638 |
| Flexural Modulus | 6600 | MPa | ASTM D790 |
| Flexural Strength | 180 | MPa | ASTM D790 |
| Compressive Strength | 170 | MPa | ASTM D695 |
| Poisson's Ratio | 0.37 | ASTM E132 | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.35 | ||
| vs. Steel - Static | 0.35 | ||
| Flexural Elongation at Break | 3.4 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 230 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 180 | V | ASTM D3638 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 290 to 320 | °C | |
| Middle Temperature | 290 to 320 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VDM87-30E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TRANSMARE® BIO M106 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| EVAL™ F171 | Kuraray Co., Ltd. | EVOH | EVAL™ |
| INNOPOL® PP CS 2-9514 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| OmniPro™ CPP GRC40 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |