Exxtral™ Performance Polyolefin HMU202
| Category: | TPO , Polypropylene, Compounded (TPO) |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Exxtral™ Performance Polyolefin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RWp35V_Exxtral-Performance-Polyolefin-HMU202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A special thermoplastic polyolefin black resin with high rigidity and low emission performance is suitable for automotive HVAC and parts under the hood. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | 3260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Complete Break) | 3.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Legal statement |
|---|
| 本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用本产品不宜在与食品接触的应用中使用。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 1500-55D | RTP Company | TPEE | RTP |
| Scolefin 64 C 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| EPO-TEK® OG159-2 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| KOCETAL® WR701LODG | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Lucent PP CPP-310 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |