Generic PEKK - Carbon Fiber
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RWYQ39_Generic-PEKK---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PEKK - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 to 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.050 to 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 to 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1100 to 26500 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.0 to 2.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 24.5 to 31000 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 210 to 245 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 to 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 313 to 330 | °C | ASTM D648 |
| Glass Transition Temperature | 160 to 163 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx WP63E40 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| Teflon® PTFE DISP 33 | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| AEI TP543C | AEI Compounds Limited | PE, Unspecified | AEI |
| AKROMID® A3 GF 25 1 L black (4672) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| Fainplast PVC FK 70 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |