Staramide ACF6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RWHIcR_Staramide-ACF6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide ACF6 is a 30 % Carbon Fiber Reinforced Polyamide 66 injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.040 to 0.080 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 4.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 250 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 19500 | MPa | ISO 178 |
| Flexural Stress | 360 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3(23°C) | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -40°C | 6.0 | kJ/m² | |
| -20°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 260 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 257 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 255 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.4E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 6 | > 4.3E+3 | ohms | IEC 60093 |
| Volume Resistivity | > 4.3E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 |
| 6 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 1310 | Huntsman Corporation | PAO | REXtac® APAO |
| Weatherflex™ CS1522WX NTL70B | Colorite Polymers | PVC, Flexible | Weatherflex™ |
| Geon™ Vinyl Rigid Extrusion 85857 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| OTECH PVC OE8050 - Calendering | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| LNP™ LUBRICOMP™ OCL36 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |