SUMIKAEXCEL® PES 3600G
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKAEXCEL® PES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RVKGu9_SUMIKAEXCEL-PES-3600G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUMIKAEXCEL® PES 3600G is a Polyethersulfone (PESU) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of SUMIKAEXCEL® PES 3600G are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption (24 hr) | 0.43 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 84.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2550 | MPa | ASTM D790 |
| Flexural Strength | 129 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 203 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -50 to 150°C | 5.5E-5 | cm/cm/°C | |
| Transverse : 50 to 150°C | 5.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Arc Resistance | 70.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.460 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 to 330 | °C | |
| Middle Temperature | 330 to 360 | °C | |
| Front Temperature | 330 to 360 | °C | |
| Nozzle Temperature | 330 to 360 | °C | |
| Processing (Melt) Temp | 350 to 360 | °C | |
| Mold Temperature | 120 to 150 | °C | |
| Injection Pressure | 98.0 to 137 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 49.0 to 68.6 | MPa | |
| Back Pressure | 4.90 to 9.80 | MPa | |
| Screw Speed | 50 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LDPE 535I | The Dow Chemical Company | LDPE | DOW™ LDPE |
| NatureFlex™ NVS 120 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Nypol® PA A3 ST VRM0076 NR325 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Ateva® 1811 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Strator® A-3 HI N7 | Solvay Specialty Polymers | Nylon 66 | Strator® |