Di-Pak™ E-4565-3
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RVB9bW_Di-Pak-E-4565-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DI-PAK E-4500 SERIES Flexible, 45, 65 and, 95 shore A hardness, potting and encapsulating systems. Flame retardant (FR), accelerated 3 minute (-3) gel time, and black or unpigmented versions are available. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.20 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 17 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 80 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 3.0 | min | ASTM D2971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Shock Test | Pass |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4.14 | MPa | ASTM D638 |
| Tensile Strength | 6.21 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 14.4 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.23 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.9E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 14 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 2.50 | ||
| 100 kHz | 2.40 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.023 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 670 | cP | ASTM D4878 |
| Demold Time (21°C) | 30 to 60 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEKK Plus® KK827H-BK | Polymics, Ltd. | PAEK | Pyramid™ PEKK Plus® |
| Resinoid 1382 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| SNOLEN® EB 0.45/54 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Badamid® LA70 H | Bada AG | Nylon 66 | Badamid® |
| INVISION™ GX 5058G6 | A. Schulman Inc. | TPE | INVISION™ |