Hostacom ERC 475L NAT
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RUZ4cc_HostacomERC475LNAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom ERC 475L nat is a 28% mineral filled PP copolymer with medium melt flow rate. The product exhibits a very low shrinkage close to ABS and an excellent impact strength. The material is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density (23°C) | 1.11 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 13.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | MPa | |
| Tensile Strength (Yield, 23°C) | 21.0 | MPa | |
| Tensile Elongation (Yield, 23°C) | 6.0 | % | |
| Flexural Modulus (23°C) | 1900 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 0°C | 9.0 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | |||
| 0°C | 80 | kJ/m² | ISO 179 |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 90.0 | °C | |
| 1.8 MPa, not annealed | 50.0 | °C | |
| Vicat Softening Temperature | 50.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 MG 30 | RTP Company | ABS | RTP |
| SEETEC EVA VC710 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| LNP™ THERMOCOMP™ LX09404 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| Durethan® AKV 15 FN 00 000000 | LANXESS GmbH | Nylon 66 | Durethan® |
| Moplen EP548S | LyondellBasell Industries | PP Impact Copolymer | Moplen |