Electrafil® TPX-PPO/HIPS-03015
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RTkDyq_Electrafil-TPX-PPO-HIPS-03015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil® TPX-PPO/HIPS-03015 is a Polyphenylene Ether + PS (PPE+PS) product filled with carbon fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 131 | °C | |
| 1.8 MPa, Unannealed | 121 | °C | |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+5 | ohms·cm | ASTM D257 |
| Static Decay | |||
| -- | Not Tested | sec | MIL B-81705C |
| [5000V - < 50V] | 20 | msec | FTMS 101B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 2.01 mm | 5V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R210A80UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| Radilon® S HS 100 P NAT | Radici Plastics | Nylon 6 | Radilon® |
| Chemical Resources SAN2500 | Chemical Resources, Inc. | SAN | Chemical Resources |
| Karina IVORY PVC COMPOUND 105800-35/ 1-B-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Stat-Tech™ PA66 C10 black (EM10001793BI) | PolyOne Corporation | Nylon 66 | Stat-Tech™ |