Toughblend® PA6-1900B
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Toughblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RTbDxz_Toughblend-PA6-1900B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughblend® PA6-1900B is a glass fiber reinforced compound which is a great alternation to metal replacement application. This grade offers superb high impact strength, excellent stiffness, high heat resistance with good wear resistance properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 232 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 15000 | MPa | ASTM D790 |
| Flexural Strength | 348 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 410 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 212 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 260 to 265 | °C | |
| Front Temperature | 265 to 275 | °C | |
| Nozzle Temperature | 275 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PP ABS HI112H | Performance Plastics, Ltd. | ABS | PP ABS |
| Prime Polypro™ J106G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Scolefin 54 T 10-9 | Ravago Group | PP Homopolymer | Scolefin |
| Akulon® Ultraflow K-FKMV5 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| InVento® 0814FR | Synthos S.A. | PS (EPS) | InVento® |