TAIRISAN NX3200
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRISAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RTGx0G_TAIRISAN-NX3200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC SAN resin NX3200 meets the requirements of UL, SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| 23°C | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/5.0 kg | 1.5 | g/10 min | |
| 220°C/10.0 kg | 15 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 83 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 78.5 | MPa | ASTM D638 |
| 23°C | 78.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 3620 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 118 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 18 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 94.0 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 210 to 250 | °C | |
| Middle Temperature | 210 to 250 | °C | |
| Front Temperature | 210 to 250 | °C | |
| Nozzle Temperature | 210 to 250 | °C | |
| Processing (Melt) Temp | < 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 68.6 to 123 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C | |
| Melt Temperature | < 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 500P | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| XYRON™ L565V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Ultramid® B36 01 | BASF Corporation | Nylon 6 | Ultramid® |
| BITONER® BT-1102 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Plaslube® PA6/6 CF20 TL15 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |