Eraclene® FC 82
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RStKV1_Eraclene-FC-82.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene FC 82 is a high density polyethylene resin (HDPE), with antioxidants, suitable for blown film extrusion. Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high film strength. Main Application Films produced by Eraclene FC 82 are recommended for high strength grocery sacks, shopping bags, notion and millinery bags. The excellent balance between drawability and bubble stability makes Eraclene FC 82 perfect for manufacturing of high strength thin films (shopping bags, bags on the reel, lamination film). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | |
| 190°C/21.6 kg | 23 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 650 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 800 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 500 | % | |
| TD : Break, 25 µm, Blown Film | 650 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 70 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 10.0 | kN/m | |
| TD : 25.0 µm | 25.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature | 135 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA211G25H | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Dryflex® A2 600450 | ELASTO | SEBS | Dryflex® |
| Haysite BMC 14100 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| KumhoSunny PC HCG2510FR | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Sylvin 7844-70C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |