Durethan® BG 30 FN05 000000

Category:	Nylon 6 , Polyamide 6
Manufacturer:	LANXESS GmbH
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RS53Qu_DurethanBG30FN05000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PA 6, 30 % glass, injection molding, halogen free flame retardant, low tendency to warp

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	Flame retardancy
Features	Low warpage Halogen-free Flame retardancy
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding
Resin ID (ISO 1043)	PA G FR (30)

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.41	--	g/cm³	ISO 1183
Apparent Density	0.70	--	g/cm³	ISO 60
Molding Shrinkage				ISO 2577
Vertical flow direction : 260°C, 2.00mm ¹	0.80	--	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.20	--	%	ISO 2577
Flow direction : 260°C, 2.00mm ³	0.80	--	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.20	--	%	ISO 2577

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	5400	2000	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	75.0	30.0	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	2.4	> 20	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	5200	2000	MPa	ISO 178/A
Flexural Stress				ISO 178/A
3.5% strain, 23°C	--	40.0	MPa	ISO 178/A
23°C ⁶	120	45.0	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁷(23°C)	3.3	7.0	%	ISO 178/A

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6, GFHR, 12-050, G30	--		ISO 1874

Injection	Dry	Unit	Test Method
Admissible Residence Time at Tmax		min
Residual Moisture Content	0.030 - 0.070	%	Karl Fisher

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	< 10	< 10	kJ/m²	ISO 179/1eA
23°C	< 10	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	45	28	kJ/m²	ISO 179/1eU
23°C	55	70	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-30°C	< 10	< 10	kJ/m²	ISO 180/1A
23°C	< 10	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength (23°C)	45	45	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	95.0	--	°C	ISO 75-2/A
Vicat Softening Temperature	195	--	°C	ISO 306/B120
Ball Pressure Test (201°C)	Pass	--		IEC 60695-10-2
Melting Temperature ⁸	222	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 55°C	6.0E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	7.0E-5	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Comparative Tracking Index (CTI)	PLC 0	--		UL 746
Comparative Tracking Index (Solution A)	550	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.400 mm	V-0	--		UL 94
0.750 mm	V-0	--		UL 94
1.50 mm	V-0	--		UL 94
3.00 mm	V-0	--		UL 94
Glow Wire Flammability Index				IEC 60695-2-12
0.400 mm	960	--	°C	IEC 60695-2-12
0.750 mm	960	--	°C	IEC 60695-2-12
1.50 mm	960	--	°C	IEC 60695-2-12
3.00 mm	960	--	°C	IEC 60695-2-12
Glow Wire Ignition Temperature				IEC 60695-2-13
0.400 mm	960	--	°C	IEC 60695-2-13
0.750 mm	900	--	°C	IEC 60695-2-13
1.50 mm	800	--	°C	IEC 60695-2-13
3.00 mm	800	--	°C	IEC 60695-2-13

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	250 - 270	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
TPC PVC SG580	Thai Plastics and Chemicals Public Company Limited	PVC Homopolymer	TPC PVC
UBESTA 3020 LU1X3	UBE Engineering Plastics, S.A.	Nylon 12	UBESTA
Anjaconduct® 150-FR/KF1E6	Almaak International GmbH	PC	Anjaconduct®
HOPELEX LX-7603	Lotte Chemical Corporation	PC	HOPELEX
PELPRENE™ P40H-05	TOYOBO America, Inc.	TPEE	PELPRENE™